Strong and weak ferromagnetic of cobalt ferrite: Structural, magnetic properties and reflection loss characteristic

Johan, Akmal and Setiabudidaya, Dedi and Arsyad, Fitri Suryani and Ramlan, Ramlan and Adi, Wisnu Ari (2023) Strong and weak ferromagnetic of cobalt ferrite: Structural, magnetic properties and reflection loss characteristic. Materials Chemistry and Physics, 295 (127086). pp. 1-14. ISSN 0254-0584, e-ISSN: 1879-3312

[thumbnail of Turnitin] Text (Turnitin)
Turnitin A1. Strong and weak ferromagnetic of cobalt ferrite_ Structural, magnetic properties and reflection loss characteristic.pdf - Other

Download (6MB)

Abstract

In this research, we investigated the effect of strong and weak ferromagnetic cobalt zinc ferrite dopant ion La3+ on the reflection loss characteristics measured at the X-band frequency (8-12 GHz). Strong and weak ferromagnetic cobalt zinc ferrite dopant ion La3+ was synthesized by solid state reaction using mechanical milling technique then sintered at 1000oC for 5 hours. Single-phase cobalt ferrite Co0.75Zn0.25Fe2-xLaxO4 and Co0.25Zn0.75Fe2-xLaxO4 (x = 0.02, 0.04, 0.06, and 0.08) with a cubic structure has been successfully formed. Particle morphology and elemental composition have also observed using a scanning electron microscope and energy dispersive spectroscopy, respectively. Meanwhile magnetic properties were characterized by using vibrating sample magnetometer in the form of a hysteresis curve. The presence of Zn in the cobalt ferrite structure that can distinguish between strong and weak ferromagnetic. The results of surface morphology observations show that the sample has a relatively uniform shape and particle size distribution and the results of this elementary analysis show that the phase composition of the two types of samples is in accordance with the expected composition. This research has obtained the most optimum composition and can produce relatively large microwave absorption at the composition of Co0.75Zn0.25Fe2-xLaxO4 with the dopant ion La3+, x = 0.08 with a maximum RL value of -27dB, -25dB, and -15dB which respectively at the frequencies of 8.4 GHz, 10.2 GHz and 11.2 GHz

Item Type: Article
Uncontrolled Keywords: Cobalt ferrite, ferromagnetic, structure, magnetic, reflection loss
Subjects: #3 Repository of Lecturer Academic Credit Systems (TPAK) > Results of Ithenticate Plagiarism and Similarity Checker
Divisions: 08-Faculty of Mathematics and Natural Science > 45201-Physics (S1)
Depositing User: Akmal Johan
Date Deposited: 12 Jun 2023 09:39
Last Modified: 12 Jun 2023 09:39
URI: http://repository.unsri.ac.id/id/eprint/108833

Actions (login required)

View Item View Item