Similarity_The Effect of the Annealing Process and Mold Variations to Failure Time of CuznCast Alloy by Dynamic Load

Utami, Nurhabibah Paramitha Eka and Pratiwi, Diah Kusuma and Nasution, Jimmy Desidawansyah (2020) Similarity_The Effect of the Annealing Process and Mold Variations to Failure Time of CuznCast Alloy by Dynamic Load. warse.

Text Ithenticate The_Effect_of_Annealing_Process_and_Mold_Variation.pdf Download (2MB)

Abstract

The main objective of this study is to determine the influence of mold casting variations and the annealing process of CuZn cast alloy. The CuZn cast alloy was annealed at 400 C to 2 hours. Failure time measurement was conducted by using Torsee's Torsion Repeated and Bending Fatigue Machine with only one level of loading 3º. Microstructure analysis was performed by using an Optical microscope to analyze its correlation with the hardness value of CuZn cast alloy. The fracture Phenomenon of the fracture fatigue specimen was analyzed by using SEM. The reduction in fatigue toughness accompanied by increased flexibility in CuZn cast alloy after annealing treatment. The decrease in mechanical properties is also shown by the reduction of hardness value confirmed by changes size of its dendrite arm spacing. The results of the investigation revealed. The results showed a significant influence of the annealing process and mold variations on the failure time and mechanical properties of CuZn cast alloy.

Item Type:	Other
Uncontrolled Keywords:	CuZn Cast Alloy, Annealing, Failure time
Subjects:	#3 Repository of Lecturer Academic Credit Systems (TPAK) > Results of Ithenticate Plagiarism and Similarity Checker
Divisions:	03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User:	Dr. Ir. Diah Kusuma Pratiwi
Date Deposited:	31 Jul 2023 08:31
Last Modified:	31 Jul 2023 08:31
URI:	http://repository.unsri.ac.id/id/eprint/111968

Actions (login required)

View Item