KAPABILITAS HIDROKSI LAPIS GANDA Zn/Al DAN Zn/Cr SEBAGAI MATERIAL PENYIMPAN HIDROGEN

NAFISYAH, WINI and Lesbani, Aldes and Hidayati, Nurlisa (2018) KAPABILITAS HIDROKSI LAPIS GANDA Zn/Al DAN Zn/Cr SEBAGAI MATERIAL PENYIMPAN HIDROGEN. Undergraduate thesis, Sriwijaya University.

Preview	Text RAMA_47201_08031281419020_0012087401_0009117201_01_front_ref.pdf - Accepted Version Available under License Creative Commons Public Domain Dedication. Download (311kB) | Preview
	Text RAMA_47201_08031281419020_0012087401_0009117201_02.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (196kB) | Request a copy
	Text RAMA_47201_08031281419020_0012087401_0009117201_03.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (91kB) | Request a copy
	Text RAMA_47201_08031281419020_0012087401_0009117201_04.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (223kB) | Request a copy
	Text RAMA_47201_08031281419020_0012087401_0009117201_05.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (64kB) | Request a copy
	Text RAMA_47201_08031281419020_0012087401_0009117201_06_ref.pdf - Bibliography Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (87kB) | Request a copy
	Text RAMA_47201_08031281419020_0012087401_0009117201_07_lamp.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (703kB) | Request a copy

Abstract

The synthesis of layered double hydroxide Zn/Al and Zn/Cr has been done. The result by using XRD characterization was showed succesfully appear in 2θ at 10º and 10º with the basal spasing of layered double hydroxide Zn/Al is 7.574 Ǻ and layered double hydroxide Zn/Cr is 7.32 Ǻ. The characterization by using BET showed the surface area of Zn/Al 9.4117 m2/g and Zn/Cr 118.9524 m2/g. The characterization using XRF showed the composition of Zn/Al (3:1) that consists of zinc 91.48% & alumunium 2.9 % , Zn/Cr (2:1) that consists of zinc 81.13% and also chromium 16.7 %. Characterization by using FT-IR showed that the spesific area of layered double hydroxide appears at 3300-3800 cm-1 as the peak of OH, anion NO3 - at 1381 cm-1, and also the vibration appears below 1000 cm-1 from M-O bonding. Zn/Cr has the best result as the hydrogen storage in the pressure 2 bar, 90 minutes, and 200 mesh produced the hydrogen capacity 69.3959 mg/g. The optimum condition of layered double hydroxide Zn/Al as the hydrogen storage was formed at pressure 1 bar, 120 minutes, and 200 mesh produced the hydrogen capacity 64.4743 mg/g. Zn/Al and Zn/Cr has the hydrogen capacity higher than diatomic gas such as oxygen or nitrogen, so layered double hydroxide Zn/Al and Zn/Cr more selective to hydrogen than oxygen and nitrogen. This is due to the involvement of hydrogen bonds beside physical adsorption in the hydrogen storage process by Zn/Al and Zn/Cr.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Layered double hydroxide , adsorption, hydrogen.
Subjects:	Q Science > QD Chemistry > QD625-655 Radiation chemistry Q Science > QD Chemistry > QD71-142 Analytical chemistry
Divisions:	08-Faculty of Mathematics and Natural Science > 47201-Chemistry (S1)
Depositing User:	Mrs Dies Meirita Sari
Date Deposited:	20 Aug 2019 05:12
Last Modified:	20 Aug 2019 05:12
URI:	http://repository.unsri.ac.id/id/eprint/4629

Actions (login required)

View Item