Sulfate Resistance of Fly Ash-Based Geopolymer Mortar

Saloma, Saloma and Iqbal, Maulid Muhammad and Aqil, Ibnu (2017) Sulfate Resistance of Fly Ash-Based Geopolymer Mortar. AIP Conference Proceedings, 1885. 020038-1-020038-7.

[thumbnail of AIP 1885, 020038 (2017) Saloma, Maulid M. Iqbal, Ibnu Aqil.pdf]
Preview
Text
AIP 1885, 020038 (2017) Saloma, Maulid M. Iqbal, Ibnu Aqil.pdf - Published Version

Download (1MB) | Preview

Abstract

This paper presents sulfuric acid attack of fly ash-based geopolymer mortar. Precursor used in this study was fly ash, and activator used was NaOH and Na2SiO3. The ratio of activator/precursor, ratio of Na2SiO3/NaOH, and ratio of fine aggregate/precursor is 0.42, 2.00, and 2.00, respectively. The molar concentration of NaOH which was used were 8, 10, 12, 14, and 16 M. This study used cube specimen with 5 cm x 5 cm x 5 cm. The results showed that the higher the molar concentration of NaOH, the lower the weight loss. Maximum percentage of weight loss is 3.54% occured for the specimen with molar concentration of NaOH 8 M. The compressive strength for all specimens decreased due to the longer duration of immersion in sulfuric acid solution. However, this percentage of decreasing for compressive strength will be as lower as increasing the molar concentration of NaOH used. The maximum percentage of decreasing is 35.49% for specimen with NaOH 8 M with 90 days of immersion.

Item Type: Article
Subjects: T Technology > TH Building construction > TH1000-1725 Systems of building construction Including fireproof construction, concrete construction
Divisions: 03-Faculty of Engineering > 22101-Civil Engineering (S2)
03-Faculty of Engineering > 22201-Civil Engineering (S1)
Depositing User: Saloma Hasyim
Date Deposited: 04 Jun 2021 12:01
Last Modified: 04 Jun 2021 12:01
URI: http://repository.unsri.ac.id/id/eprint/47603

Actions (login required)

View Item View Item