Saloma, Saloma and Hanafiah, Hanafiah and Putra, Fungki Nopreal (2017) The Effect of Polypropylene Fiber on Mechanical Properties of Reactive Powder Concrete. AIP Conference Proceedings, 1885. 020093-1-020093-6.
Preview |
Text
AIP 1885, 020093 (2017) Saloma, Hanafiah, Fungki Nopreal Putra.pdf - Published Version Download (997kB) | Preview |
Abstract
Reactive Powder Concrete (RPC) was known as concrete with very dense in microstructure and having high value in compressive strength due to the utilization of very fine materials. One of the weakness of RPC is very brittle. To improve the ductility could used polypropylene fiber. In this research, the various weight of the polypropylene fiber used were 0.4 kg, 0.6 kg, and 0.8 kg per cubic metre of concrete. From this study, RPC mixture with 0.8 kg polypropylene fiber yielded maximum value, e.g the compressive strength was 103.253 MPa, modulus of elasticity was 45.252 MPa, splitting tensile strength was 5.91 MPa, and flexural strength was 9.56 MPa.
| Item Type: | Article |
|---|---|
| Subjects: | T Technology > TH Building construction > TH1000-1725 Systems of building construction Including fireproof construction, concrete construction |
| Divisions: | 03-Faculty of Engineering > 22101-Civil Engineering (S2) 03-Faculty of Engineering > 22201-Civil Engineering (S1) |
| Depositing User: | Saloma Hasyim |
| Date Deposited: | 04 Jun 2021 12:02 |
| Last Modified: | 04 Jun 2021 12:02 |
| URI: | http://repository.unsri.ac.id/id/eprint/47609 |
Actions (login required)
 |
View Item |