ANALISA PENGARUH KUAT ARUS PADA PROSES ELECTROPLATING BAJA LAPIS CHROM TERHADAP KETEBALAN DAN KEKASARAN LAPISAN

WIBOWO, ARIO and Alian, Helmy (2018) ANALISA PENGARUH KUAT ARUS PADA PROSES ELECTROPLATING BAJA LAPIS CHROM TERHADAP KETEBALAN DAN KEKASARAN LAPISAN. Undergraduate thesis, Sriwijaya University.

[img]
Preview
Text
RAMA_21201_03051181320013_0015105904_01_front_ref.pdf - Accepted Version
Available under License Creative Commons Public Domain Dedication.

Download (1MB) | Preview
[img] Text
RAMA_21201_03051181320013_0015105904_02.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (275kB) | Request a copy
[img] Text
RAMA_21201_03051181320013_0015105904_03.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (89kB) | Request a copy
[img] Text
RAMA_21201_03051181320013_0015105904_04.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (69kB) | Request a copy
[img] Text
RAMA_21201_03051181320013_0015105904_05.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (49kB) | Request a copy
[img] Text
RAMA_21201_03051181320013_0015105904_06.ref.pdf - Bibliography
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (48kB) | Request a copy
[img] Text
RAMA_21201_03051181320013_0015105904_07_lamp.pdf - Accepted Version
Restricted to Repository staff only
Available under License Creative Commons Public Domain Dedication.

Download (7MB) | Request a copy

Abstract

In the industrial world, the metal coating process is very concerned about the quality of metal, unfortunately the metal quality will decrease due to its environmental influence, causing the efficiency of a metal is not the maximum one of its factors the occurrence of corrosion. The problems encountered in the metal coating that occurs is the occurrence of corrosion and layer defects are not evenly distributed on the specimen. This study aims to study the chrom layer on the electroplating process. In this research, low carbon steel JIS G 3101 SS 400, specimen size 100 mm x 40 mm x 4 mm with current density of coating thickness and roughness. Current density is used 15 amperes, 20 amperes, 35 amperes and time 20, 40, 60 minutes. The research process that is, literature study, do testing chemical composition, chromic Acid solution, Sulfuric Acid, and testing the weight, thickness and roughness of the coating. The result of the research shows that the longer the dyeing time, the higher the coating weight, thickness and surface roughness value.The weight value is 2,431 grams, the thickness is 0.0188 μm and the roughness of 20.6 μm at the current density variation 15 Amper time 60 minutes.

Item Type: Thesis (Undergraduate)
Uncontrolled Keywords: Electroplating, Chromic Acid, Low Carbon Steel, Strong Current, Time
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA165 Engineering instruments, meters, etc. Industrial instrumentation
Divisions: Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User: Mr. Afrizal Aziz
Date Deposited: 05 Sep 2019 02:22
Last Modified: 05 Sep 2019 02:22
URI: http://repository.unsri.ac.id/id/eprint/6378

Actions (login required)

View Item View Item