PENGARUH WAKTU TAHAN POURING TERHADAP STRUKTUR MIKRO PLAT TWDI 1 mm

Sulamet-Ariobimo, Rianti D. and Soedarsono, Johny W. and Suharno, Bambang (2011) PENGARUH WAKTU TAHAN POURING TERHADAP STRUKTUR MIKRO PLAT TWDI 1 mm. In: Prosiding Seminar Nasional AVoER ke-3. Fakultas Teknik Universitas Sriwijaya, Palembang, pp. 416-421. ISBN 979-587-395-4

[thumbnail of Pages_from_PROSIDING_AVOER_2011-42.pdf]
Preview
Text
Pages_from_PROSIDING_AVOER_2011-42.pdf

Download (705kB) | Preview

Abstract

Fading in ductile iron production covers the loss of inoculation and nodulation effectiveness. The main factors of fading are process time and temperature including rest time between tapping and pouring. This research conducted to see the effect of time rest between tapping and pouring process to the completion of inoculation and nodulation process. Analysis was done on 1 mm plates of TWDI casting process. The liquid metal came from 1 bath. Variations of casting condition were presented. The Tapping temperature was 1550OC. The pouring temperature varied of the first bath was 1399OC, 1389OC, 1385OC and 1381OC. Rest time was analysis as the temperature differences between tapping temperature and pouring temperature. The completion of inoculation and nodulation process were seen in nodule count and nodularity. The result shows that longer rest time lay between tapping and pouring will cause disturbance to inoculation and nodulation process. Apart from that the level of tapping temperature which is also inoculation temperature should be maintained.

Item Type: Book Section
Additional Information: Jurusan Teknik Mesin, Fakultas Teknologi Industri, Universitas Trisakti Kampus A, Jl. Kyai Tapa No. 1, Grogol, Jakarta 1440, Indonesia Departemen Metallurgi dan Material, Fakultas Teknik, Universitas Indonesia Kampus UI Depok, Depok 16424, Indonesia Politeknik Negeri Jakarta
Uncontrolled Keywords: 1 mm TWDI plate, nodulation, inoculation, process condition, nodule count, nodularity, tapping, pouring
Subjects: T Technology > T Technology (General) > T1-995 Technology (General)
T Technology > TJ Mechanical engineering and machinery > TJ1-1570 Mechanical engineering and machinery
T Technology > TN Mining engineering. Metallurgy > TN1-997 Mining engineering. Metallurgy
Divisions: 03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User: backup admin
Date Deposited: 09 Jan 2020 12:15
Last Modified: 09 Jan 2020 12:15
URI: http://repository.unsri.ac.id/id/eprint/23329

Actions (login required)

View Item View Item