STUDI PENGARUH TEMPERATUR KOMPAKSI PADA PEMBUATAN KERAMIK HIDROKSIAPATIT MELALUI PROSES SINTERING DINGIN

OCTAPIA, ANI and Gunawan, Gunawan (2021) STUDI PENGARUH TEMPERATUR KOMPAKSI PADA PEMBUATAN KERAMIK HIDROKSIAPATIT MELALUI PROSES SINTERING DINGIN. Undergraduate thesis, Sriwijaya University.

	Text RAMA_21201_03051181722074.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (7MB) | Request a copy
Preview	Text RAMA_21201_03051181722074_0007057702_01_front_ref.pdf - Accepted Version Available under License Creative Commons Public Domain Dedication. Download (7MB) | Preview
	Text RAMA_21201_03051181722074_0007057702_02.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (1MB) | Request a copy
	Text RAMA_21201_03051181722074_0007057702_03.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (1MB) | Request a copy
	Text RAMA_21201_03051181722074_0007057702_04.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (1MB) | Request a copy
	Text RAMA_21201_03051181722074_0007057702_05.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (213kB) | Request a copy
	Text RAMA_21201_03051181722074_0007057702_06_ref.pdf - Bibliography Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (730kB) | Request a copy
	Text RAMA_21201_03051181722074_0007057702_07_lamp.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (1MB) | Request a copy
	Text RAMA_21201_03051181722074_TURNITIN.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (8MB) | Request a copy

Abstract

Research has been carried out on the manufacture of hydroxyapatite ceramics by the cold sintering method. In the manufacture of hydroxyapatite ceramics by cold sintering method using low-temperature techniques. The research was conducted at temperatures of 1500C, 2000C, and 2500C with a pressure of 600 Mpa in a holding time of 10 minutes. Sample analysis was performed using density, compression, and XRD tests. From the results obtained from the density test at each temperature, the average percentage value of porosity at temperatures of 1500C, 2000C, and 2500C decreased because it was influenced by the increase in temperature given during compaction. In testing the compressive strength at each pressure of the hydroxyapatite ceramic with temperatures of 1500C, 2000C, and 2500C at a pressure of 600 MPa, in this test, the graph experienced a decrease in the average value of the compressive strength caused by the same thing, which was influenced by high temperatures during cold sintering compaction. In the XRD test, it was found that the resulting spectrum corresponds to the graph generated by the ICDD standard.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Hidroksiapatit, Kompaksi, Sintering Dingin, Tulang Sapi, Temperatur
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ1-1570 Mechanical engineering and machinery
Divisions:	03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User:	Ani Octapia
Date Deposited:	01 Sep 2021 02:50
Last Modified:	01 Sep 2021 02:50
URI:	http://repository.unsri.ac.id/id/eprint/53046

Actions (login required)

View Item