PENGARUH VARIASI W/B TERHADAP KARAKTERISTIK SELF COMPACTING CONCRETE DENGAN ABU CANGKANG SAWIT

NURAZIZAH, ERVI TRI ROMAYNI and Muliawan, Sutanto and Nurjannah, Siti Aisyah (2021) PENGARUH VARIASI W/B TERHADAP KARAKTERISTIK SELF COMPACTING CONCRETE DENGAN ABU CANGKANG SAWIT. Undergraduate thesis, Sriwijaya University.

	Text RAMA_22201_03011281621070.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (10MB) | Request a copy
	Text RAMA_22201_03011281621070 _TURNITIN.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (5MB) | Request a copy
Preview	Text RAMA_22201_03011281621070_0024045604_8884960018_01_front_ref.pdf - Accepted Version Available under License Creative Commons Public Domain Dedication. Download (2MB) | Preview
	Text RAMA_22201_03011281621070_0024045604_8884960018_02.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (283kB) | Request a copy
	Text RAMA_22201_03011281621070_0024045604_8884960018_03.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (655kB) | Request a copy
	Text RAMA_22201_03011281621070_0024045604_8884960018_04.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (251kB) | Request a copy
	Text RAMA_22201_03011281621070_0024045604_8884960018_05.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (15kB) | Request a copy
	Text RAMA_22201_03011281621070_0024045604_8884960018_06_ref.pdf - Bibliography Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (92kB) | Request a copy
	Text RAMA_22201_03011281621070_0024045604_8884960018_07_lamp.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (8MB) | Request a copy

Abstract

The study was conducted on the effect of w/b on SCC concrete with palm oil fuel ash (POFA). Variations of W/B used in the compositions of SCC were 0.325, 0.350, and 0.375. Meanwhile, the POFA used is 10% of cement total. The results showed that the variation of w/b and the use of POFA affected the workability of the concrete, that could be seen from the test of fresh concrete in the form of slump flow, V-funnel, and L-box, which showed that the higher the value of W/B, the greater the slump diameter, Test time of the funnel was got shorter and the H2/H1 ratio was got bigger. Meanwhile, the effect of POFA on the compositions of SCC was that became thicker due to the fine grains of POFA and caused more water absorption so that the results of the slump flow test and the ratio of H2/H1 could be smaller than SCC without POFA and the V-funnel could take longer. In addition, w/b also affected the compressive strength and density of concrete, the smaller the value of w/b, the higher the compressive strength, and the greater the density of the concrete. The use of POFA as a partial substitute for cement also affected the compressive strength and density produced. The highest compressive strength value was obtained when the SCC concrete used POFA at w/b 0.325 of 36.78 MPa at the age of 28 days but the density decreased when used POFA.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Self Compacting Concrete, W/B, POFA, Compressive Strength, Density
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) > TA170-171 Environmental engineering
Divisions:	03-Faculty of Engineering > 22201-Civil Engineering (S1)
Depositing User:	Users 9905 not found.
Date Deposited:	14 Jan 2021 07:50
Last Modified:	14 Jan 2021 08:10
URI:	http://repository.unsri.ac.id/id/eprint/40080

Actions (login required)

View Item