PENGARUH TEKANAN KOMPAKSI TERHADAP PEMBUATAN MAGNET PERMANEN NdFeB (NEODYMIUM IRON BORON) DARI LIMBAH JET MILL BONDED NdFeB/Nd SERTA KARAKTERISASINYA

APRILITA, RHINDA and Djauhari, Nenen Rusnaeni and Ramlan, Ramlan (2016) PENGARUH TEKANAN KOMPAKSI TERHADAP PEMBUATAN MAGNET PERMANEN NdFeB (NEODYMIUM IRON BORON) DARI LIMBAH JET MILL BONDED NdFeB/Nd SERTA KARAKTERISASINYA. Undergraduate thesis, Sriwijaya University.

	Text RAMA_45201_08021181320001.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (952kB) | Request a copy
Preview	Text RAMA_45201_08021181320001_0010046604_01_front_ref.pdf - Accepted Version Available under License Creative Commons Public Domain Dedication. Download (276kB) | Preview
	Text RAMA_45201_08021181320001_0010046604_02.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (229kB) | Request a copy
	Text RAMA_45201_08021181320001_0010046604_03.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (88kB) | Request a copy
	Text RAMA_45201_08021181320001_0010046604_04.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (241kB) | Request a copy
	Text RAMA_45201_08021181320001_0010046604_05.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (45kB) | Request a copy
	Text RAMA_45201_08021181320001_0010046604_06_ref.pdf - Bibliography Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (48kB) | Request a copy
	Text RAMA_45201_08021181320001_0010046604_07_lamp.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (413kB) | Request a copy

Abstract

Research on the manufacturing of permanent magnet NdFeB from based materials waste Jet Mill bonded NdFeB/Nd. Prepared based materials is done by using High Energy Milling (HEM) for 30 minutes then curing at a temperature 60 0C for 1 hours in the Under Vacum Dryer. Then mixing based materials with a mass 6 grams, 2 drops hardener and 4 %wt epoxy resin for later formed Cold Pressing was varied at 3 ton, 4 ton, 6 ton and 8 ton for 2 minutes with room temperature and then Annealing with temperature 100 0C for 1 hours. For characterized is done analysis Bulk Density , SEM/EDX, XRD, and Gaussmeter. Of the four variations of compaction pressure, the highest density is owned by pellet samples with 8 ton compaction pressures of 4,833 gr/cm3. The result of SEM/EDX is found that the microstructure is uneven, so there are still pores on the sample surface. As for the element content of Nd and Fe still dominate the particles with bright colors while on the particles with darker color content of C is more dominate. For XRD results it is found that the phase contained in the crystal structure there are 2 ie Nd2Fe14B and α-Fe. For the result of measurement of magnetic field strength by using gauss meter, the strongest magnetic field strength is found in 8 ton samples.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Jet Mill bonded NdFeB, Permanent Magnet, Cold Pressing.
Subjects:	Q Science > QC Physics > QC1-999 Physics Q Science > QC Physics > QC474-496.9 Radiation physics (General) Q Science > QC Physics > QC770-798 Nuclear and particle physics. Atomic energy. Radioactivity
Divisions:	08-Faculty of Mathematics and Natural Science > 45201-Physics (S1)
Depositing User:	Mrs Dies Meirita Sari
Date Deposited:	03 Dec 2019 08:22
Last Modified:	03 Dec 2019 08:22
URI:	http://repository.unsri.ac.id/id/eprint/19821

Actions (login required)

View Item