Kusuma, Fuji Hemawati and Sriyanti, ida and Edikresnha, Dhewa and Munir, Muhammad Miftahul and Khairurrijal, Khairurrijal (2016) Simply Electrospun Gelatin/Cellulose Acetate Nanofibers and their Physicochemical Characteristics (Similarity Check). Trans Tech Publications, Switzerland.
Preview |
Text
Similarity_Prosiding_Ida Sriyanti-10.pdf Download (1MB) | Preview |
Abstract
elatin in fibers form can be used for tissue engineering, wound dressing, or drug carrier. However, it is easily damaged if exposed to water. Thus, it was blended with cellulose acetate. Acetic acid was used as a solvent because it is less toxic. The mass ratios of gelatin to cellulose acetate of 10:0, 8:2, and 6:4 were as precursor solutions. Simple electrospinning was employed to produce gelatin/cellulose acetate fibers. From SEM images, it was shown that the average diameters of gelatin/cellulose acetate fibers from the precursor solutions of 10:0, 8:2, and 6:4 were 534, 649, and 765 nm, respectively. The addition of cellulose acetate increased the viscosity of gelatin/cellulose acetate solution. Moreover, gelatin mass reduction caused a decrease in conductivity of gelatin/cellulose acetate solution. Therefore, increasing in the viscosity or reducing in the conductivity of the precursor solution increased the average diameter of the gelatin/cellulose acetate fibers. The analysis of FTIR spectra showed that the structural changes of gelatin and cellulose acetate occurred after being transformed into gelatin/cellulose acetate nanofibers.
| Item Type: | Other |
|---|---|
| Subjects: | #3 Repository of Lecturer Academic Credit Systems (TPAK) > Results of Ithenticate Plagiarism and Similarity Checker |
| Divisions: | 06-Faculty of Education and Educational Science > 84103-Physics Education (S2) |
| Depositing User: | Dr Ida Sriyanti, M.Si |
| Date Deposited: | 15 Feb 2021 08:04 |
| Last Modified: | 15 Feb 2021 08:04 |
| URI: | http://repository.unsri.ac.id/id/eprint/42706 |
Actions (login required)
 |
View Item |