PENGARUH TEMPERATUR SINTERING PADA KERAMIK HIDROKSIAPATIT TERDOPING TEMBAGA 1, 1.5, DAN 2 MOL

FALAH, AFIF and Arifin, Amir (2022) PENGARUH TEMPERATUR SINTERING PADA KERAMIK HIDROKSIAPATIT TERDOPING TEMBAGA 1, 1.5, DAN 2 MOL. Undergraduate thesis, Sriwijaya University.

	Text RAMA_21201_03051381823067.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (3MB) | Request a copy
	Text RAMA_21201_03051381823067_TURNITIN.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (8MB) | Request a copy
Preview	Text RAMA_21201_03051381823067_0024097806_01_front_ref.pdf - Accepted Version Available under License Creative Commons Public Domain Dedication. Download (939kB) | Preview
	Text RAMA_21201_03051381823067_0024097806_02.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (213kB) | Request a copy
	Text RAMA_21201_03051381823067_0024097806_03.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (593kB) | Request a copy
	Text RAMA_21201_03051381823067_0024097806_04.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (960kB) | Request a copy
	Text RAMA_21201_03051381823067_0024097806_05.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (81kB) | Request a copy
	Text RAMA_21201_03051381823067_0024097806_06_ref.pdf - Bibliography Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (89kB) | Request a copy
	Text RAMA_21201_03051381823067_0024097806_07_lamp.pdf - Accepted Version Restricted to Repository staff only Available under License Creative Commons Public Domain Dedication. Download (488kB) | Request a copy

Abstract

Hydroxyapatite is a derivative of calcium phosphate and is not a small part of it is also used for coating on bones because it is very good biocompatible. Copper was chosen as undoubtedly because it works to improve angiogenic and antibacterial hydroxyapatite. The addition of copper in the biomaterial is currently being prepared because it is expected to improve the biological properties of bone graft substitutes. Copper-doped hydroxyapatite ceramics (CuHA) are made with high-temperature solid state sintering between a mixture of HA and CuO powders. This study aims to determine the effect of sintering temperature on CuHA ceramics. The synthesis of HA powder is made by the calcination method using an electric furnace with a temperature of 800°C for two hours. CuHA ceramics are made using the solid state sintering method with temperature variations of 1000, 1100, 1200°C heating rate of 10°C/min with a compaction pressure of 150 MPa and a Composition of CuO of 1.1.5 and 2 moles. From the XRD test, it can be known that the composition of the phase formed is HA (hydroxyapatite), CuO and the new phase of tricalcium phosphate. From several other tests, it is known that the greater the sintering temperature used, the smaller the percentage percentage will be between 51.304% and 45.499%. In the press test, a compressive strength value will be obtained between 23,842 to 15.88 MPa. Shrinkage results obtained shrinkage values between 58.535% to 50.875%.

Item Type:	Thesis (Undergraduate)
Uncontrolled Keywords:	Biomaterial, Hydroxyapatite, Solid State Sintering, Bovine Bone
Subjects:	T Technology > TJ Mechanical engineering and machinery > TJ1-1570 Mechanical engineering and machinery
Divisions:	03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User:	Afif Falah
Date Deposited:	23 Sep 2022 04:35
Last Modified:	23 Sep 2022 04:35
URI:	http://repository.unsri.ac.id/id/eprint/79432

Actions (login required)

View Item