Hasil Pengecekan Similaritas_Improvement Incoloy Alloy 800 Weldability After 10 Years of Service through Solution Annealing and Normalizing Method

Arifin, Amir and Gunawan, Gunawan (2023) Hasil Pengecekan Similaritas_Improvement Incoloy Alloy 800 Weldability After 10 Years of Service through Solution Annealing and Normalizing Method. Universitas Sriwijaya.

Text 05_Improvement_Incoloy Similaritas.pdf - Other Download (3MB)

Abstract

Incoloy Alloy 800 is widely utilized in the Outlet Manifold Bottom Header (OMBH) inside the primary reformer at a fertilizer plant. Primary reformers in fertilizer plants usually work at high temperatures and pressures for long periods. In this work, Solution annealing and normalizing method were conducted to improve weldability Incoloy alloy 800 after operating for ten years. Characterization of weldability properties is carried out through dye penetrant, X-ray Fluorescence, hardness, X-Ray Diffraction (XRD), and metallography observation. The annealing and normalizing result show that the weldability of Incoloy Alloy 800 increased, indicating a significant reduction in cracks on the weld zone surface. Microstructure observations revealed that microcrack was not found on the weld joint surface after Solution annealing. The maximum hardness value on the fusion zone was obtained at 187 VHN on normalizing, and minimum hardness was obtained on the nontreatment sample 156.33 VHN. Keywords: weldability, incoloy alloy 800, annealing, normalizing.

Item Type:	Other
Subjects:	#3 Repository of Lecturer Academic Credit Systems (TPAK) > Results of Ithenticate Plagiarism and Similarity Checker
Divisions:	03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User:	Amir Arifin
Date Deposited:	02 May 2023 14:43
Last Modified:	05 May 2023 06:19
URI:	http://repository.unsri.ac.id/id/eprint/98863

Actions (login required)

View Item