Hasil Pengecekan Similaritas_Failure Analysis of 304 Stainless Steel Tubes ofIntercooler Carbon Dioxide Compressor

Arifin, Amir (2023) Hasil Pengecekan Similaritas_Failure Analysis of 304 Stainless Steel Tubes ofIntercooler Carbon Dioxide Compressor. Universitas Sriwijaya.

Text 01_ Failure similaritas tes.pdf - Other Download (3MB)

Abstract

The annual inspection of the petrochemical plant revealed that SS 304 tubes at Intercooler CO2 Compressor have failed. Some heat exchanger tubes were found during inspection with circumferential cracks. Some analysis methods were performed to investigate heat exchanger tube failures, such as X-Ray diffraction analysis, XRF (X-ray fluorescence) analysis, hardness test, morphology analysis, and numerical analysis. Investigation results revealed that pitting corrosion has been found on the inner surface of the tube that an essential factor in initiating cracks. Moreover, some porosities were observed spread distributed on the surface sample, which is believed to reduce the mechanical and physical value of the material. The corrosion and the fact that cracks were initiated in the relatively small tensile loads sites suggest that the component failure resulted from chloride-induced stress corrosion cracking. Investigation results for heat exchanger parameters, chloride content, and temperature operation have become the main factor in initiating chloride stress corrosion cracking (CSCC). The operational condition of the heat exchanger should not be referred to by the tube material austenitic SS 304. Regarding the systems with SS 304 tube heat exchangers and chloride content

Item Type:	Other
Subjects:	#3 Repository of Lecturer Academic Credit Systems (TPAK) > Results of Ithenticate Plagiarism and Similarity Checker
Divisions:	03-Faculty of Engineering > 21201-Mechanical Engineering (S1)
Depositing User:	Amir Arifin
Date Deposited:	02 May 2023 07:21
Last Modified:	05 May 2023 06:42
URI:	http://repository.unsri.ac.id/id/eprint/98798

Actions (login required)

View Item